MICRALOX Accelerated Corrosion Testing Update: (1) 336 Hours of Salt Spray Test per Mil-A-8625F

MICRALOX has been tested salt spray corrosion resistance per Mil-A-8625 F.   Per Mil-A-8625F, test specimens, prepared using 3 by 10 inches panels having thickness of 0.063 inches, subjected to a 5 percent salt spray test in accordance with ASTM B 117.  After exposure of 336 hours, specimen is visually examined to determined that all of the following conditions are met:

  • Test specimens shall show no more than a total of 15 isolated pits, none larger than 0.031 inch in diameter, in a total of 150 square inches of test area grouped from five or more test pieces.
  • Test specimens shall show no more than 5 isolated pits, none larger than 0.031 inch in diameter, in a total of 30 square inches from one of more test pieces.

We are pleased to announce that MICRALOX passed 3,048 salt spray corrosion resistance hours as of October 5th.  It will be continuously going as long as we get a good result.   The report is attached for your information.  Stay tuned for further results.

Micralox Salt Spray Test Result_3048 Hrs

About Mike Sung

Chemical Engineer
This entry was posted in Newsletters, Testing, Uncategorized. Bookmark the permalink.

Leave a Reply

Fill in your details below or click an icon to log in:

WordPress.com Logo

You are commenting using your WordPress.com account. Log Out /  Change )

Google+ photo

You are commenting using your Google+ account. Log Out /  Change )

Twitter picture

You are commenting using your Twitter account. Log Out /  Change )

Facebook photo

You are commenting using your Facebook account. Log Out /  Change )

w

Connecting to %s